3D-CAM NYLON 66/6
PHYSICAL PROPERTIES
| Density | 0.039-0.0419 lb/in3 |
| Water Absorption | 0-10 % |
| Moisture Absorption at Equilibrium | 2.1-4 % |
| Water Absorption at Saturation | 0-12 % |
| Moisture Vapor Transmission | 356 cc-mil/100 in²-24hr-atm |
| Oxygen Transmission | 88.9 cc-mil/100 in²-24hr-atm |
| Environmental Stress Crack Resistance | 1000 hour |
| Linear Mold Shrinkage | 0.008-0.011 in/in |
| Linear Mold Shrinkage, Transverse | 0.01-0.011 in/in |
| Melt Flow | 60 g/10 min |
MECHANICAL PROPERTIES
| Hardness, Rockwell R | 76-118 |
| Tensile Strength, Ultimate | 4790-11600 psi |
| Tensile Strength, Yield | 2180-12300 psi |
| Elongation @ break | 5-640 % |
| Elongation @ Yield | 5-50 % |
| Tensile Modulus | 46.4-537 ksi |
| Flexural Modulus | 27.6-508 ksi |
| Flexural Yield Strength | 1310-15200 psi |
| Compressive Yield Strength | 2470 psi |
| Taber Abrasion, mg/1000 Cycles | 10 |
| Shear Strength | 8560 psi |
| Izod Impact, Notched | 0.562- NB |
| Izod Impact, Notched Low Temp | 0.918-3.5 ft-lb/in |
| Charpy Impact, Unnotched | 28.6-NB |
| Charpy Impact, Notched Low Temp | 1.9 ft-lb/in2 |
| Charpy Impact | 1.43-16.7 ft-lb/in2 |
| Coefficient of Friction, Static | 0.5-1 |
| Tensile Creep Modulus, 1 hour | 145000 psi |
| Tensile Creep Modulus, 1000 hours | 129000 psi |
ELECTRICAL PROPERTIES
| Electrical Resistivity | 1E+11-1E+15 ohm-cm |
| Dielectric Constant | 3.2-6 |
| Dielectric Constant, Low Frequency | 3.7-4.1 |
| Dielectric Strength | 457-3050 kV/in |
| Dissipation Factor | 0.02-0.3 |
| Dissipatin Factor, Low Frequency | 0.01–0.03 |
| Surface Resistance | 1E+10-1E+15 ohm |
| Comparative Tracking Index | 600 V |
THERMAL PROPERTIES
| CTE, linear 200 C | 36.1-47.2 µ in/in-°F |
| CTE, linear 20° C Transvers to Flow | 50 µ in/in-°F |
| Melting Point | 374-500°F |
| Maximum Service Temperature, Air | 135-311°F |
| Deflection Temperature at 0.46 MPa | 180-435°F |
| Deflection Temperature at 1.8 MPa | 135-194°F |
| Vicat Softening Point | 482°F |
| Flammability, UL94 | V-0 |
| Oxygen Index | 34-37% |
OPTICAL PROPERTIES
| Haze | 1-4 % |
| Gloss | 130-145% |
| Transmission, Visible | 80% |
PROCESSING PROPERTIES
| Processing Temperature | 482-536°F |
| Rear Barrel Temperature | 482°F |
| Middle Barrel Temperatue | 482°F |
| Front Barrel Temperature | 500°F |
| Mold Temperature | 122°F |
| Drying Temperature | 176°F |