Typical Properties Typical Value Standard
Specific Gravity 1.12 ASTM D 792
Water Absorption, 24 hours @ 730F 0.1 % ASTM D 570
Water Absorption, Equilibrium, 730F 0.4 % ASTM D 570
Mold Shrinkage, flow, 0.125″ 0.5-0.7 % 3D-CAM Method
Mold Shrinkage, xflow, 0.125″ 0.5-0.7 % 3D-CAM Method
Melt Flow Rate, 2300C/3.8 Kgf 7 g/10 min ASTM D 1238
Melt Flow Rate, 2600C/5.0 Kgf 24 g/10 min ASTM D 1238


Typical Properties Typical Value Standard
Tensile Stress, Yield, Type l, 2.0 in/min 8400 psi ASTM D 638
Tensile Strain, Yield, Type l, 2.0 in/min 5 % ASTM D 638
Tensile Strain, brk, Type l, 2.0 in/min 80 % ASTM D 638
Tensile Modulus, 2.0 in/min 360000 psi ASTM D 638
Flexural Modulus, 0.05 in/min, 2 in span 360000 psi ASTM D 790
Flexural Stress, yld, 0.05 in/min, 2 in span 13200 psi ASTM D 790
Izod Impact, Notched, 730F 10 ft-lb/in ASTM D 256
Izod Impact, notched, -220F 2 ft-lb/in ASTM D 256
Instrumented Impact Total Energy, 730F 480 in-lb ASTM D 3763
Instrumented Impact Total Energy, -220F 360 in-lb ASTM D 3763


Electrical Resistivity 1E+14-1E+17 ohm-cm
Dielectric Constant 2.2-2.3
Dielectric Constant, Low Frequency 2.3
Dielectric Strength 559-3560 kV/in
Dissipation Factor 0.0002-0.002
Dissipatin Factor, Low Frequency 0.00007–0.00081
Surface Resistance 1E+10-1E+14 ohm
Arc Resistance 136 sec
Comparative Tracking Index 600 V


CTE, linear 200 C 13.9-103 µ in/in-°F
Heat Capacity 0.478 BTU/lb-°F
Thermal Conductivity 0.694-0.902 BTU-in/hr-ft²-°F
Melting Point 266-334°F
Maximum Service Temperature, Air 111-298°F
Deflection Temperature at 0.46 MPa 55.4-460°F
Deflection Temperature at 1.8 MPa 98.6-298°F
Vicat Softening Point 95-298°F
UL RTI, Electrical 149°F
UL RTI, Mechanical with Impact 149°F
UL RTI, Mechanical without Impact 149°F
Flammability, UL94 HB


Haze 11 %


Processing Temperature 396-486°F
Rear Barrel Temperature 428°F
Middle Barrel Temperatue 428°F
Front Barrel Temperature 428°F
Nozzle Temperature 428°F
Mold Temperature 95-120°F
Drying Temperature 180°F