PHYSICAL PROPERTIES
| Density | 0.0415-0.043 lb/in3 |
| Water Absorption | .3-2 % |
| Moisture Absorption at Equilibrium | 0.3-0.33 % |
| Linear Mold Shrinkage | 0.003-0.0065 in/in |
| Melt Flow | 0.9-27 g/10 min |
MECHANICAL PROPERTIES
| Density | 0.0415-0.043 lb/in3 |
| Water Absorption | .3-2 % |
| Moisture Absorption at Equilibrium | 0.3-0.33 % |
| Linear Mold Shrinkage | 0.003-0.0065 in/in |
| Melt Flow | 0.9-27 g/10 min |
ELECTRICAL PROPERTIES
| Electrical Resistivity | 1E+14-1E+15 ohm-cm |
| Dielectric Constant | 2.8-4 |
| Dielectric Constant, Low Frequency | 3-4 |
| Dielectric Strength | 450-1520 kV/in |
| Dissipation Factor | 0.03-0.55 |
| Dissipatin Factor, Low Frequency | 0.05-0.55 |
| Surface Resistance | 1E+14-1E+16 ohm |
| Comparative Tracking Index | 600 V |
THERMAL PROPERTIES
| CTE, linear 200 C | 33.3-72.2 µ in/in-°F |
| Heat Capacity | 0.349-0.351 BTU/lb-°F |
| Thermal Conductivity | 1.32-1.67 BTU-in/hr-ft²-°F |
| Melting Point | 266°F |
| Maximum Service Temperature, Air | 106-217°F |
| Deflection Temperature at 0.46 MPa | 176-217°F |
| Deflection Temperature at 1.8 MPa | 106-212°F |
| Vicat Softening Point | 117-243°F |
| Glass Temperature | 212-221°F |
| Flammability, UL94 | HB |
| Oxygen Index | 18% |
OPTICAL PROPERTIES
| Refractive Index | 1.49-1.498 |
| Haze | 1-96% |
| Transmission, Visible | 80-93% |
PROCESSING PROPERTIES
| Processing Temperature | 469-482°F |