PHYSICAL PROPERTIES
| Density |
0.039-0.0419 lb/in3 |
| Water Absorption |
0-10 % |
| Moisture Absorption at Equilibrium |
2.1-4 % |
| Water Absorption at Saturation |
0-12 % |
| Moisture Vapor Transmission |
356 cc-mil/100 in²-24hr-atm |
| Oxygen Transmission |
88.9 cc-mil/100 in²-24hr-atm |
| Environmental Stress Crack Resistance |
1000 hour |
| Linear Mold Shrinkage |
0.008-0.011 in/in |
| Linear Mold Shrinkage, Transverse |
0.01-0.011 in/in |
| Melt Flow |
60 g/10 min |
MECHANICAL PROPERTIES
| Hardness, Rockwell R |
76-118 |
| Tensile Strength, Ultimate |
4790-11600 psi |
| Tensile Strength, Yield |
2180-12300 psi |
| Elongation @ break |
5-640 % |
| Elongation @ Yield |
5-50 % |
| Tensile Modulus |
46.4-537 ksi |
| Flexural Modulus |
27.6-508 ksi |
| Flexural Yield Strength |
1310-15200 psi |
| Compressive Yield Strength |
2470 psi |
| Taber Abrasion, mg/1000 Cycles |
10 |
| Shear Strength |
8560 psi |
| Izod Impact, Notched |
0.562- NB |
| Izod Impact, Notched Low Temp |
0.918-3.5 ft-lb/in |
| Charpy Impact, Unnotched |
28.6-NB |
| Charpy Impact, Notched Low Temp |
1.9 ft-lb/in2 |
| Charpy Impact |
1.43-16.7 ft-lb/in2 |
| Coefficient of Friction, Static |
0.5-1 |
| Tensile Creep Modulus, 1 hour |
145000 psi |
| Tensile Creep Modulus, 1000 hours |
129000 psi |
ELECTRICAL PROPERTIES
| Electrical Resistivity |
1E+11-1E+15 ohm-cm |
| Dielectric Constant |
3.2-6 |
| Dielectric Constant, Low Frequency |
3.7-4.1 |
| Dielectric Strength |
457-3050 kV/in |
| Dissipation Factor |
0.02-0.3 |
| Dissipatin Factor, Low Frequency |
0.01–0.03 |
| Surface Resistance |
1E+10-1E+15 ohm |
| Comparative Tracking Index |
600 V |
THERMAL PROPERTIES
| CTE, linear 200 C |
36.1-47.2 µ in/in-°F |
| CTE, linear 20° C Transvers to Flow |
50 µ in/in-°F |
| Melting Point |
374-500°F |
| Maximum Service Temperature, Air |
135-311°F |
| Deflection Temperature at 0.46 MPa |
180-435°F |
| Deflection Temperature at 1.8 MPa |
135-194°F |
| Vicat Softening Point |
482°F |
| Flammability, UL94 |
V-0 |
| Oxygen Index |
34-37% |
OPTICAL PROPERTIES
| Haze |
1-4 % |
| Gloss |
130-145% |
| Transmission, Visible |
80% |
PROCESSING PROPERTIES
| Processing Temperature |
482-536°F |
| Rear Barrel Temperature |
482°F |
| Middle Barrel Temperatue |
482°F |
| Front Barrel Temperature |
500°F |
| Mold Temperature |
122°F |
| Drying Temperature |
176°F |
this is t
|